生产的用丁基橡胶是一种用于中空玻璃的单组分、无溶剂、不雾化、不硫化和永久性塑料密封剂。

The produced butyl rubber is a single component, solvent-free, non atomizing, non vulcanizing, and permanent plastic sealant used for insulating glass.

热熔丁基密封胶在较宽的温度范围内保持其塑性和密封性，表面不开裂、不硬化。由于其极低的水蒸气透过率，可与弹性密封胶一起形成优良的防潮体系。

Hot melt butyl sealant maintains its plasticity and sealing properties over a wide temperature range, with no surface cracking or hardening. Due to its extremely low water vapor transmittance, it can form an excellent moisture-proof system together with elastic sealant.

因此密封效果好，质量容易保证。不需要熟化期，节省了占地面积，降低了生产成本；它是一种环保产品，无废弃物，环境清洁。

Therefore, the sealing effect is good and the quality is easy to ensure. No need for maturation period, saving land area and reducing production costs; It is an environmentally friendly product with no waste and a clean environment.

中空玻璃用丁基胶粘剂是双组分聚氨酯密封胶、双组分聚硫密封胶、双组分硅酮密封胶和中空玻璃热熔胶制作中空玻璃第一道密封的必备胶粘剂。根据中空玻璃丁基胶涂机胶仓的大小，选择不同规格的中空玻璃丁基胶。

Butyl adhesive for insulating glass is an essential adhesive for the first sealing of insulating glass, which includes two-component polyurethane sealant, two-component polysulfide sealant, two-component silicone sealant, and insulating glass hot melt adhesive. Select different specifications of insulating glass butyl adhesive according to the size of the adhesive compartment of the insulating glass butyl adhesive coating machine.

用中空玻璃丁基橡胶制作中空玻璃时，应注意以下7点:

When making insulating glass with butyl rubber, the following 7 points should be noted:

1.中空玻璃丁基橡胶-使用注意事项。清洁铝隔条以备后用。

1. Hollow glass butyl rubber - Precautions for use. Clean the aluminum partition strip for future use.

2.将丁基热熔密封胶放入挤出机料筒，预热至130-140℃。恒温器保持恒温后，在冲胶条检查均匀性和连续性时，将胶条涂在铝隔断槽上，用干净的玻璃压住，稍冷却后形成中空玻璃半成品。

2. Put the butyl hot melt sealant into the extruder barrel and preheat it to 130-140 ℃. After maintaining a constant temperature with the thermostat, when checking the uniformity and continuity of the adhesive strip, apply the strip to the aluminum partition groove, press it with clean glass, and cool it slightly to form a semi-finished hollow glass product.

3.外层密封胶涂覆固化后，即得到成品中空玻璃。

After the outer layer of sealant is coated and cured, the finished hollow glass is obtained.

4.使用进口快胶机时，胶筒温度应提高10-15℃，挤压压力应由150兆帕调整到170-200兆帕，以使胶条均匀生产。

When using an imported fast glue machine, the temperature of the rubber cylinder should be increased by 10-15 ℃, and the extrusion pressure should be adjusted from 150 megapascals to 170-200 megapascals to ensure uniform production of the rubber strip.

5.服用和使用丁基热熔密封胶时，请清洁双手。密封胶表面不应沾有灰尘、油和溶剂(如丙酮、汽油等)。).戴上不起毛的手套，涂抹。

5. When taking and using butyl hot melt sealant, please clean your hands. The surface of the sealant should not be contaminated with dust, oil, or solvents (such as acetone, gasoline, etc.) Wear lint free gloves and apply.

6.触摸热胶时要小心烧伤。接触胶水的手套应干净，没有毛刺或其他容易粘在胶水上的污染物。

Be careful of burns when touching hot glue. Gloves that come into contact with glue should be clean and free of burrs or other contaminants that can easily stick to the glue.